What is SAE 1010?

What is SAE 1010?

SAE 1010 hardness is a carbon steel expressed for major starting into wrought products. It has a very great electrical conductivity among shaped carbon or non-alloy steels. In addition, it has an honestly low current conductivity and can have a justly low ductile strength.

What is the tensile strength of 1010 steel?

365 MPa 52900 psi
Mechanical Properties

Properties Metric Imperial
Tensile strength 365 MPa 52900 psi
Yield strength (depending on temper) 305 MPa 44200 psi
Elastic modulus 190-210 Gpa 27557-30458 ksi
Bulk modulus (typical for steel) 140 GPa 20300 ksi

What is 1010 Cold rolled steel?

Sometimes referred to as Shim Stock, Cold Rolled 1010 Steel is oiled to resist rust and stain. Typically utilized in tool and die shops, machine repair and bearing adjustments, Cold Rolled 1010 Steel is rolled to precision tolerances. Cold Rolled 1010 Steel is used in low strength applications.

How hard is 1010 steel?

A stress relief anneal may be done at 1000 F and slow cooled. In the full annealed condition 1010 steel has a tensile strength of about 45 ksi….1010 Carbon Steels Material Property Data Sheet – Product availability and request a quote.

Density (lb / cu. in.) 0.284
Specific Gravity 7.86

How do you heat treat 1010 steel?

Heat Treatment of AISI 1010

  1. Normalize at 1725° to 1775°F (941° to 968°C) before air cooling.
  2. Anneal at 1650° to 1750°F (899° to 954°C) before furnace cooling.
  3. Harden at 1650° to 1700°F (899° to 927°C) before quenching in water, brine or caustic.
  4. Can be case hardened.

What is c1018 steel used for?

It provides high surface hardness and a soft core to parts that include worms, dogs, pins, liners, machinery parts, special bolts, ratchets, chain pins, oil tool slips, tie rods, anchor pins, studs etc. It is used to improve drilling, machining, threading and punching processes.

Can C1018 be hardened?

General Characteristics of Low-Carbon Steel 1018 C1018 is a general purpose carbon steel that is easily machined and welded and may be hardened by carburizing and by other surface-hardening methods.

Is C1018 cold rolled?

C1018 is a general purpose low carbon steel with good case hardening qualities. With higher manganese, 1018 is better steel for carburized parts, since it produces a harder and more uniform case. It also has higher mechanical properties and better machinability due to the cold drawing process.